  一、Clay brick insulation

  Clay insulation bricks using advanced manufacturing technology, its features are: uniform organizational structure, high mechanical strength. Low thermal conductivity, widely used in all kinds of glass furnace, saving more than 30%, is the ideal energy-saving insulation material.

    
Index Products
Numbering Code
Al2O3 ≥%
Fe2O3 ≤%
Bulk density Bulk Density ≥g/cm3
Cold crushing strength Cold Crushing Strength ≥Mpa
Thermal Conductivity Thermal Conductivity (W/m.k)
Reheating Linear change of less than 2% of the test temperatureTest Temperature when the Permanent Linear Change on Reheating is less than 2% ℃
Clay brick insulation:Fireclay Insulation Bricks
NG-0.6
38
60
0.6
1.47
0.25
1200
NG-0.7
38
60
0.7
1.96
0.35
1250
NG-0.8
38
60
0.8
2.45
0.35
1250
NG-0.9
38
60
0.9
2.45
0.40
1300
NG-1.0
38
60
1.0
2.94
0.50
1350

  二、Poly light alumina brick

  Poly light brick high aluminum large with good insulation properties, high temperature furnace to shorten the heating time, reduce heat diffusion furnace temperature protection features. Main widely used in the bottom of the furnace heat insulation.

 Index Products Numbering Code Al2O3 ≥% Fe2O3 ≤% Bulk densityBulk Density ≥g/cm3 Cold crushing strength Cold Crushing Strength ≥Mpa The highest temperature Max Service Temperature ℃ Thermal ConductivityThermal Conductivity (Average Temp350±25℃) (≤W/m.k)
Poly light alumina brick Poly Light High Alumina Firebrick LG-0.5 48 2.0 0.5 1.5 1250 0.25
LG-0.6 48 2.0 0.6 2.0 1350 0.30
LG-0.7 48 2.0 0.7 2.5 1350 0.35
LG-0.8 48 2.0 0.8 3.0 1400 0.35
LG-0.9 48 2.0 0.9 3.5 1400 0.45
LG-1.0 48 2.0 1.0 4.0 1400 0.50
LG-1.3 50 1.3 1.3 8.0 1450 0.60

  三、Quality silica brick

  Silica brick kiln is the key refractory glass and other industrial furnace high temperature zones. Quality silica brick has three high, four low, a good main features. Namely: high-purity dense (good thermal conductivity), high load soft, high tridymite content; low true density, low expansion, low creep, low residual quartz content; the correct size, pure color, good appearance.

project ITEMS
Glass furnace brick For Glass kiln
Trademark Brand
BG-96A
BG-95A
BG-96B
BG-95B
SiO2  %   ≥
96
95
96
95
Fe2O3 %   ≤
0.3
0.5
0.3
0.5
Al2O3+TiO2+R2O  %
0.5
Load softening starting temperature RUL(0.2MPa)T1,℃
1680
1680
1670
1650

Apparent porosity %APP

APPARENT POROSITY
22
Cold crushing strength CCS ,Mpa ≥
35
Bulk density Bulk Density ≥g/cm3
1.86
1.86
1.86
1.86

  四、Magnesia brick

Magnesia brick magnesia brick is divided into ordinary and fused magnesia brick, magnesia content of 95% or less of a dense dead burned magnesia, magnesium content of more than 95% high purity magnesia or fused magnesia, high-pressure molding, ultra high temperature burn the product is prepared into anti-erosion ability, widely used in anti-alkali and other key parts of the regenerator.

  五、Corundum mullite

  Corundum, corundum - mullite composite products, fused and sintered mullite mullite products have good thermal shock resistance, high temperature strength and density, the glass furnace, furnace, chemical furnace, metallurgical industrial furnaces of choice for high-quality materials.

  六、Sillimanite

  The internal structure of the product good elasticity, can effectively overcome the mechanical stress due to the special manner and fixed temperature gradient caused by low penetration, and thus infiltration tin bath base phenomenon rarely avoid nepheline “Peeling ”。Mainly used for float glass kiln feeding channel, initial thermal storage room.

project ITEM
index Behaviors
Physical indicators
Physical Properties
Refractoriness(℃)Refractoriness
1790
Bulk density(g/cm3)Bulk Density
2.53
Apparent porosity(%)Apparent Porosity
18
Room temperature flexural strength(Mpa)Cold Tucking strengh
10
Cold crushing strength(Mpa)Cold Crushing strengh
100
Reheating Linear Change(%)1100℃*2h Permanent Linear change on reheating
±0.1
Thermal shock resistance(次)1000℃水冷Thermal shock stability 1000℃ water
≥25
chemical composition(%)
Chemical Composition
Al2O3
65
SiO2
32
Fe2O3
0.3
Na2O+K2O
≤1.0
CaO+MgO
≤1.0

  七、Zircon brick

  Zircon refractory products are acidic material is a natural zircon sand as raw material products. Zirconium refractory slag resistance good, small coefficient of thermal expansion, thermal conductivity decreases with increasing temperature, high load softening temperature, strong abrasion resistance, thermal shock resistance, which has become in various industrial fields important material.

  八、Low-porosity clay brick for glass furnace

  This product uses special shock refractory castable molding process to produce glass with a low porosity clay brick kiln, and the appearance of its physical and chemical indicators are better than national standards. Anti-corrosive liquid glass of the product is superior to conventional slip cast molding process and ramming molding process products, especially for use in masonry glass kiln bottom, middle and lower thermal storage wall, the lower checker bricks, arch support and other parts.